#banner { position: relative; width: 1003px; height: 200px; overflow: hidden; margin: 0 auto; } #banner_list img { border: 0px; } #banner_bg { position: absolute; bottom: 0; background-color: #000; height: 30px; filter: Alpha(Opacity=30); opacity: 0.3; z-index: 1000; cursor: pointer; width: 1003px; } #banner_info { position: absolute; bottom: 0; left: 5px; height: 22px; color: #fff; z-index: 1001; cursor: pointer } #banner_text { position: absolute; width: 120px; z-index: 1002; right: 3px; bottom: 3px; } #banner ul { position: absolute; list-style-type: none; filter: Alpha(Opacity=80); opacity: 0.8; z-index: 1002; margin: 0; padding: 0; bottom: 3px; right: 20px; } #banner ul li { padding: 0px 3px; float: left; display: block; border: #e5eaff 1px solid; background: #f8fafa; cursor: pointer; font-size: 12px; } #banner ul li.on { background: #dfdfdf } #banner_list a { position: absolute; }
当前位置:首页 >新闻中心 > 20Cr2Ni4A合金鋼化學成分,20Cr2Ni4A合金鋼力學特性

20Cr2Ni4A合金鋼化學成分,20Cr2Ni4A合金鋼力學特性

2020-07-31 05:47   评论:39 点击:418

20Cr2Ni4A合金鋼化學成分,20Cr2Ni4A合金鋼力學特性

一、20Cr2Ni4A合金鋼力學特性:   抗拉強度σb(MPa):1483   條件屈服強度σ0.2(MPa):1292   伸長率δ5(%):13   斷麵收縮率ψ(%):57   衝擊韌性值αkv(J/cm2):75   硬度:434HB   試樣尺寸:某試料 二、20Cr2Ni4A合金鋼化學成分:   碳C:0.17~0.23   矽Si:0.17~0.37   錳Mn :0.30~0.60   硫S:≤0.03   磷P:≤0.03   鉻Cr:1.25~1.65   鎳Ni:3.25~3.65。

40CrNiMoA合金鋼特點 一 、40CrNiMoA鋼密度:   40CrNiMoA合金鋼密度為 :ρ(kg/m3):約7830。 二、40CrNiMoA鋼材性能:   彈性模量(GPa):209   抗拉強度σb(MPa):≥980(100)   屈服強度σs(MPa):≥835(85)   伸長率δ5(%) :≥12   斷麵收縮率ψ(%) :≥55   衝擊功Akv(J):≥78   衝擊韌性值αkv(J/cm²):≥98(10)   試樣尺寸:試樣毛坯尺寸為25mm   熱處理:(淬火850度;冷卻劑:油;回火溫度600度;冷卻劑:水、油);   鋼材退火或高溫回火供應狀態布氏硬度GBW≤269 。 三 、40CrNiMoA合金鋼理論重量計算方法:   40CrNiMoA扁鋼:每米重量(公斤)=0.00785×厚度×邊寬   40CrNiMoA管材:每米重量(公斤)=0.02466×壁厚×(外徑-壁厚)   40CrNiMoA棒材:直徑*直徑*0.00617=kg/米(每米的重量)   40CrNiMoA板材:寬*高*0.00785=kg/米(每米的重量)

上一篇:140*16鋼管直徑是多少 140*16北京40Cr鋼管價格 140*16標準YB/T5035鋼管
下一篇:降低304不鏽鋼管生產成本主要有以下幾種途徑

我来说两句已有39条评论,点击全部查看
我的态度:

网站首页| 公司概况| 荣誉资质| 产品展示| 销售网络| 公司团队| 公司新闻| 钢管知识| 联系我们| 网站地图